Effect of Pulse Current Mode on Microstructure, Composition and Corrosion Performance of the Coatings Produced by Plasma Electrolytic Oxidation on AZ…
2019
Plasma electrolytic oxidation (PEO) coatings were grown on AZ31 Mg alloy in a silicate-based electrolyte containing KF using unipolar and bipolar (usual and soft-sparking) waveforms. The coatings were dual-layered consisting of MgO, MgF2 and Mg2SiO4 phases. Surface morphology of the coatings was a net-like (scaffold) containing a micro-pores network, micro-cracks and granules of oxide compounds. Deep pores were observed in the coating produced by unipolar and usual bipolar waveforms. The soft-sparking eliminated the deep pores and produced the lowest porosity in the coatings. It was found that the corrosion performance of the coatings evaluated using EIS in 3.5 wt. % NaCl solution is mostly…
Corrosion and wear resistance of coatings produced on AZ31 Mg alloy by plasma electrolytic oxidation in silicate-based K2TiF6 containing solution: Ef…
2022
Abstract In this research, plasma electrolytic oxidation coatings were prepared on AZ31 Mg alloy in a silicate-based solution containing K2TiF6 using bipolar and soft sparking waveforms with 10, 20, and 30% cathodic duty cycles. The coatings displayed a net-like surface morphology consisted of irregular micro-pores, micro-cracks, fused oxide particles, and a sintered structure. Due to the incorporation of TiO2 colloidal particles and the cathodic pulse repair effect, most of the micro-pores were sealed. Long-term corrosion performance of the coatings was investigated using electrochemical impedance spectroscopy during immersion in 3.5 wt.% NaCl solution up to 14 days. The coating grown by t…
The Effect of Electrolytic Solution Composition on the Structure, Corrosion, and Wear Resistance of PEO Coatings on AZ31 Magnesium Alloy
2020
Plasma electrolytic oxidation coatings were prepared in aluminate, phosphate, and silicate-based electrolytic solutions using a soft-sparking regime in a multi-frequency stepped process to compare the structure, corrosion, and wear characteristics of the obtained coatings on AZ31 magnesium alloy. The XRD results indicated that all coatings consist of MgO and MgF2, while specific products such as Mg2SiO4, MgSiO3, Mg2P2O7, and MgAl2O4 were also present in specimens based on the selected solution. Surface morphology of the obtained coatings was strongly affected by the electrolyte composition. Aluminate-containing coating showed volcano-like, nodular particles and craters distributed over the …
The multi-effects of K2TiF6 additive on the properties of PEO coatings on AZ31 Mg alloy
2020
Abstract Plasma electrolytic oxidation of AZ31 Mg alloy was performed in an alkaline silicate-based solution containing various concentrations of K2TiF6 using unipolar waveform at a constant voltage. The surface morphology of all coatings was rough and contained a micro-pore network, micro-cracks, and granules of oxide compounds in different diameters and micro-pore levels. The coating is composed of MgO, MgF2, Mg2SiO4, SiO2 (amorphous), and TiO2 (crystalline and amorphous) phases. The average thickness of the coatings was increased by adding the K2TiF6, where EDS results showed that a skinny fluoride-rich passive layer forms. With increasing time and reaching the final potential, the TiO2 …